The composition consists of chlorinated rubber, plasticizer, titanium dioxide, coloring pigment, additives and solvents, etc..
The main characteristics of water vapor and oxygen permeability to paint film is low, with excellent water resistance, corrosion resistance, and decorative; Dry is fast, several times faster than the dry of alcoholic acid paint; It has excellent low-temperature construction performance and can be constructed in -20 ~ 50 environment. The paint film layer and the layer are mutually soluble and have excellent interlayer adhesion. When repairing the coating on the old paint film of chlorinated rubber, it is not necessary to remove the solid old paint film and maintain it easily. Good endurance and durability.
Uses for various land steel structures such as waterline, hull, superstructure, power plant, steel plant, dock steel structure, chemical plant, bridge, container, hydraulic steel gate, factory building, oil tank outer wall, dry gas cabinet. For protection and decorative paint.
appearance
Product Code Product Code Color and Appearance
J43-32(605-3) 08-22 Orange, semi-light
J43-32(610-3) 08-24 Soy green, semi-light
J43-32(626) 08-28 Iron Red, Semi-Light
J43-32(626-3) 08-30 Iron Red, Semi-Light
J43-32(629) 08-31 Green, semi-light
J43-32(629-3) 08-33 Green, semi-light
J43-32(634-3) 08-35 Big Red, Semi-Light
J43-32(662-3) 08-38 Orange red, semi-light
J43-32(663) 08-39 Steel ash, semi-light
J43-32(663-3) 08-40 Steel ash, semi-light
J43-32(667-3) 08-42 White, semi-light
J43-32(669) 08-43 Blue gray, semi-light
J43-32(670) 08-46 Light ash, semi-light
J43-32(670-3) 08-47 Light ash, semi-light
J43-32(671-3) 08-49 Sea Blue, Semi-Light
J43-32(675-3) 08-51 medium gray, semi-light
J43-32(682-3) 08-53 Black, semi-light
Construction parameters
Product code volume solid * % dry film thickness μm wet film thickness μm theoretical dosage g/m2
605-3 44 ± 3 70 158 222
610-3 42 ± 3 70 168 236
626 42 ± 3 40 95 121
626-3 42 ± 3 70 167 234
629 42 ± 3 40 95 121
629-3 42 ± 3 70 167 234
634-3 42 ± 3 70 167 234
662-3 42 ± 3 70 167 234
663 40 ± 3 40 100 127
663-3 42 ± 3 70 167 234
667-3 42 ± 3 70 167 234
669 42 ± 3 40 95 121
670 42 ± 3 40 95 121
670-3 42 ± 3 70 167 234
671-3 42 ± 3 70 167 234
675-3 42 ± 3 70 167 234
682-3. 42 ± 3 70 167 234
:: Volume solids(as specified in GB/T9272 eqv IS 03233:1998)
Flash point 31 °C
Dry time(25 °C)
Dry ≤ 2H
Dry ≤ 12h
Duplication interval
Temperature 5 °C 20 °C 30 °C
Minimum 24h12h6h
Maximum unlimited
It is recommended that the number of coating channels be 1-2 and the thickness of the dry film be 70-140 μm. In the construction, it is better to use high pressure and no gas spraying.
The front track is equipped with paint 615-1, 615-2 aluminum powder chlorinated rubber rust proof paint for anti-rust primer paint, and 616 chlorinated rubber iron-red thick plasma anti-rust paint for intermediate layer paint. Or H06-04 epoxy rust resistant paint as primer, 842 epoxy cloud iron rust resistant paint for the middle layer paint.
The surface treatment front paint should be completely dry; Except for all the grease and dirt on the paint.
The temperature of the substrate under construction conditions must be higher than 3 °C above the dew point; Relative humidity not more than 85 %
Painting Method
No air spray thinner 101 thinner; 5 % dilution(in paint weight); Nozzle diameter 0.4-0 .5 mm; Spray pressure 15-20 MPa(with 150-200 kg/cm2)
Air spray thinner 101 thinner; Dilution 0-10 %(in paint weight); Nozzle diameter 2.0-3 .0 mm; Air pressure: 0.3-0 .4 MPa(about 3-4 kg/cm2)
The thickness of the recommended dry film can not be reached with a roll / brush coating; diluent 101 diluent; Dilution 0-3 %(in paint weight).
Cleaning agent 101 diluent
Safety measures refer to the product safety technical specifications of Zhongsheng Paint(Ningbo) Co., Ltd..
Packaging 22kg
Warranty period 12 months